Carbonfiber 1 Cold end kept at 80mK, warm end kept at 1K. Power measured to be 3.28uW. Stray heating effects from leads are negligible. Value is in good agreement...
Carbonfiber 3 Another sample with 12 carbonfiber rods from UPenn. This time the thermal conductance was huge, so series resistance at room temperature was changed...
G10 1 (The first fiberglass sample) Photo of the sample Fiberglass (G10) sample sent from UPenn, this material is suspected to be the reason for unexpected therm...
Hex Aluminum Flex Two different resistance vs temperature measurements were done on different parts of Hex Aluminum flex. One measurement had 24 traces connected ...
Hex Aluminum Flex Critical Current Measurement Same two bundles of traces on the hex flex from NIST. This time excitation current dependence of resistance of flex...
NIST PA2 Pixel One of the pixels sent from NIST to test the critical temperature of TESs corresponding to two polarizations. These were connected to channels 1 an...
NIST TES devices First Tc measurement was done with the cooldown that started on October 11, 2013. Two (out of three) samples sent from NIST, V13 and V15, were us...
USF1 "Bad" and USF3 "Not Bad" Flex Two semihex flexes brought from Princeton on 12/08/13 to see how uniform is their critical temperature and critical current. Th...
Tc measurements Superconducting critical temperature (Tc) measurement of various Aluminum Flexes and TES (transition edge sensor) devices. Resistances are measure...
This page has the graphs of how temperature at four different parts of the dilution refrigerator changed with time during the original cool down with Anssi in Apr...